Kevlar Chopped Strands for Friction Material

5mm  kevlar chopped strands for friction material was chopped in 5mm by a unique cutting equipment&period of time This fiber has higher toughness and modulus&comma sturdy hydrogen bonding strength&comma power up to 28 g&bought or much more&comma energy is five-6 moments of metal wire&periodspecific modulus 2-three moments of it&commatoughness 2 times of it whilst bodyweight is just one&sol5 of the wire&periodContinuous utilizing temperature selection is incredibly wide&comma long working in the range of -196 ºC to 204 ºC&commano decomposition and melting at high temperature of 560 ºC&commastrength can preserve seventy five&percnt via 100 hours at 200 ºC&periodalso has excellent chemical solvent resistance&comma resisting acid and alkali&comma anti-aging&comma good adhesion to rubber&interval Generally it is used as a reinforcing content in the fields of thermoplastics&comma thermosetting plastics&comma substantial-temperature composite structures&comma brake pads&comma clutch linings&comma friction substance&comma put on-resistant filler&comma cable sheathing&comma gaskets&comma slot insulation&comma stage insulation barrier&comma interturn insulation and so on&period of time
 
Technical specs&colon

Design&colon XGPF1205
Colour&colon yellowish
Fiber type&colon Para-aramid
Density&lparg&solcc&rpar 1&period47
CZPT density of mono filament&lparD&rpar  one&period5
Filament diameter&lparμm&rpar 12
Fiber length&lparmm&rpar 5
Tensile strength&lpar cN&soldtex&rpar 19&period4-21
Elongation at break&lpar&percnt&rpar 2&period5-three&period84
Tensile modulus&lparGPa&rpar eighty~one hundred twenty
Shrinkage&lpar&percnt&rpar <0&period2&lpar190ºC×15m&rpar
Moisture &lpar&percnt&rpar&colon <0&period2

Application FIELDS&colon
1&periodCZPT CZPTs&commathermosetting resin&commafriction resources&comma automotive brakes&commacomposite components and Kevlar bolstered paper&period 
two&periodreinforcing supplies&commaconstruction&commarubber&commareinforced cable&commacable and other higher-intensity rope&period
3&periodcomposite content with resin or rubber&commacan considerably minimize the fat&commaincrease loading excess weight&commasuitable for the production of aerospace equipment&commahigh-speed trains and yachts shell&period of time
4&periodFriction and sealing components&commafriction resources reinforced fiber&comma considerably improved put on resistance&commasuitable for substantial temperature problems&time period
 
STORAGE&colon
The 5mm kevlar chopped strands for friction materials should be maintain dry in their original baggage and saved in a appropriate place&commapreferably at area temperature with 35-65&percnt relative humidity&periodAvoid the sunlight&comma rain and fire

PACKAGING&colon
one&periodInner black plastic movie luggage&commanet excess weight five&period00kg&periodgross weight five&period20kg&period of time
two&periodBag dimension&colon43&ast36&ast28cm&commanet bodyweight 120&period00kg&periodgross bodyweight one hundred fifty&period00kg&period of time

Shipment AND TRANSPORTATION&colon
1&periodShipment by sea&colonfor sea transportation&commagenerally 20 pallets&lpareach 180kg&periodtwo layers&rparbe loaded into 20 toes container&periodtotal web weight is 2400kg&interval
2&periodtransportation by truck&colonfor truck transportation&commagenerally loading in buck with 7layers&commaabout 3120kg
three&periodtransportation by rail&colonfor rail transportation&commagenerally loading in buck&commaabout 6720kg&period

Kevlar Chopped Strands for Friction Material